H02 - Rod / Bar -
Tensile Strength:
Yield Strength:
Rockwell Hardness B Scales:
84 ksi
60 ksi - 0.5% Ext. under load
90
Chemical Composition (%max., unless shown as range or min.)
Need to send a drawing?
We are now accepting the following file types:
Cu(1) Fe Pb Mn Sn Zn Min./Max. 57.0-60.0 .40-1.3 .50-1.0 .05-.50 .50-1.5 Rem.
Nominal 58.5 .8 .7 .27 1.0 38.7
(1) Cu value includes Ag.
Note: Cu + Sum of Named Elements, 99.5% min.
Joining Techniques
Soldering
Brazing
Oxyacetylene Welding
Gas Shielded Arc Welding
Spot Weld
Capacity for Being Cold Worked
Capacity for Being Hot Formed
Forgeability Rating
Machinability Rating
Suitability
Excellent
Excellent
Good
Fair
Good
Poor
Excellent
80
60
Mechanical Properties (measured at room temperature, 68 F (20 C)
Fabrication Properties
Typical for 1" Bar
Physical Properties
Melting Point - Liquidus
Melting Point - Solidus
Density
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Modulas of Elasticity in Tension Modulus of Rigidity
US Customary
1630 F
1590 F
0.302 lb/in3 at 68 F
24 %IACS @ 68 F
61.0 Btu · ft/(hr · ft2·oF)at 68F
11.8 ·10-6 per oF (68-572 F)
15000 ksi
5600 ksi
Melting Point - Liquidus
Melting Point - Solidus
Density
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Modulas of Elasticity in Tension
Modulus of Rigidity
Metric
890 C
865 C
8.36 gm/cm3 @ 20 C
0.139 MegaSiemens/cm @ 20 C
105.7 W/m · oK at 20 C
20.4 ·10-6 per oC (20-300 C)
103400 MPa
38600 MPa